GB / T 21832オーステナイト/フェライト(二重)グレードのステンレス鋼溶接チューブおよびパイプ
仕様 :
材質: 329J3L 1.4462
サイズ範囲 :外 径: 4-1200mm
WT: 0.3-200mm
一般的な長さ: 3 - 12m
許容差:
次の表または顧客の要求に従って。
機械的性質
No. | Unified digital code |
Steel Grade |
Recommended heat treatment system | Tensile property | Hardness | ||||
Tensile strength Rm/(N/mm2) |
Non proportional extension strength Rp0.2/(N/mm2) |
Elongation | HBW | HRC | |||||
≥ | ≤ | ||||||||
1 | S21953 | 022Cr19Ni5Mo3Si2N | 980℃~1040℃ | Rapid cooling | 630 | 440 | 30 | 290 | 30 |
2 | S22253 | 022Cr22Ni5Mo3N | 1020℃~1100℃ | Rapid cooling | 620 | 450 | 25 | 290 | 30 |
3 | S22053 | 022Cr23Ni5Mo3N | 1020℃~1100℃ | Rapid cooling | 655 | 485 | 25 | 290 | 30 |
4 | S23043 | 022Cr23Ni4MoCuN | 925℃~1050℃ |
Rapid cooling D≤25mm |
690 | 450 | 25 | - | - |
Rapid cooling D>25mm |
600 | 400 | 25 | 290 | 30 | ||||
5 | S22553 | 022Cr25Ni6Mo2N | 1050℃~1100℃ | Rapid cooling | 690 | 450 | 25 | 280 | - |
6 | S22583 | 022Cr25Ni7Mo3WCuN | 1020℃~1100℃ | Rapid cooling | 690 | 450 | 25 | 290 | 30 |
7 | S25554 | 03Cr25Ni6Mo3Cu2N | ≥1040℃ | Rapid cooling | 760 | 550 | 15 | 297 | 31 |
8 | S25073 | 022Cr25Ni7Mo4N | 1025℃~1125℃ | Rapid cooling | 800 | 500 | 15 | 300 | 32 |
9 | S27603 | 022Cr25Ni7Mo4WCuN | 1100℃~1140℃ | Rapid cooling | 750 | 550 | 25 | 300 | - |
No hardness required of the steel grade, only have to provide the measured data, not as the delivery conditions |
スチールグレード参考表
No. | China | USA | Japan | Europe | |
Unified digital code | Steel Gade | ASTM A790-05a | JIS G3463.2005 | EN 10217-7.2005 | |
1 | S21953 | 022Cr19Ni5Mo3Si2N | S31500 | - | - |
2 | S22253 | 022Cr22Ni5Mo3N | S31803 | SUS329J3LTB |
X2CrNiMoN22-5-3 1.4462 |
3 | S22053 | 022Cr23Ni5Mo3N | S32205 | - | - |
4 | S23043 | 022Cr23Ni4MoCuN | S32304 | - |
X2CrNiN23-4 1.4362 |
5 | S22553 | 022Cr25Ni6Mo2N | S31200 | - | - |
6 | S22583 | 022Cr25Ni7Mo3WCuN | S31260 | SUS329J4LTB | - |
7 | S25554 | 03Cr25Ni6Mo3Cu2N | S32550 | - | - |
8 | S25073 | 022Cr25Ni7Mo4N | S32750 | - |
X2CrNiMoN25-7-4 1.4410 |
9 | S27603 | 022Cr25Ni7Mo4WCuN | S32760 | - |
X2CrNiMoCuWN25-7-4 1.4501 |
スチールチューブの推奨熱処理システムと機械的特性
Number | Steel grade |
Recommended Heat treatment system |
Tensile property | Hardness | ||||
Tensile strength Rm/(N/mm²) |
Specifies the non-proportional extension strength Rp0.2/MPa |
Elongation A/% |
HBW | HRC | ||||
No less than | No more than | |||||||
1 | 022Cr19Ni5Mo3Si2N | 980℃~1040℃ | Quenching | 630 | 440 | 30 | 290 | 30 |
2 | 022Cr22Ni5Mo3N | 1020℃~1100℃ | Quenching | 620 | 450 | 25 | 290 | 30 |
3 | 022Cr23Ni5Mo3N | 1020℃~1100℃ | Quenching | 655 | 485 | 25 | 290 | 30 |
4 | 022Cr23Ni4MoCuN | 925℃~1050℃ | Quenching | 690 | 450 | 25 | 290 | 30 |
5 | 022Cr25Ni6Mo2N | 1050℃~1100℃ | Quenching | 600 | 400 | 25 | 280 | - |
6 | 022Cr25Ni7Mo3WCuN | 1020℃%~1100℃ | Quenching | 690 | 450 | 25 | 290 | 30 |
7 | 03Cr25Ni6Mo3Cu2N | ≥1040℃ | Quenching | 760 | 450 | 25 | 297 | - |
8 | 022Cr25Ni7Mo4N | 1025℃~1125℃ | Quenching | 800 | 550 | 15 | 300 | 32 |
9 | 022Cr25Ni7Mo4WCuN | 1100℃~1140℃ | Quenching | 750 | 550 | 25 | 300 | - |
異なる規格の二重のステンレススチールブランドのコントラストテーブル
Number | China | US | Japan | Europe |
Steel grade in this standard | ASTM A790-05a | JIS G3463:2006 | EN 10217-7:2005 | |
1 | 022Cr19Ni5Mo3Si2N | S31500 | - | - |
2 | 022Cr22Ni5Mo3N | S31803 | SUS329J3LTH |
X2CrNiMoN22-5-3 1.4462 |
3 | 022Cr23Ni5Mo3N | S32205 | - | - |
4 | 022Cr23Ni4MoCuN | S32304 |
|
X2CrNiN234 1.4362 |
5 | 022Cr25Ni6Mo2N | S31200 | - | - |
6 | 022Cr25Ni7Mo3WCuN | S31260 | SUS329J4LTB | - |
7 | 03Cr25Ni6Mo3Cu2N | S32550 | - | - |
8 | 022Cr25Ni7Mo4N | S32750 | - |
X2CrNiMoN25-7-4 1.4410 |
9 | 022Cr25Ni7Mo4WCuN | S32760 | - |
X2CrNiMnCuWN25-7-4 1.4501 |
製造方法:片面または両面自動アーク溶接
技術的供給条件: 熱処理後の酸洗
/アプリケーションの分野で広く使用されています:圧力機器、液体配送、熱交換器